Polymer Systems
Technology Limited
Biomaterials
Medical Implants
Adhesives
MED-1137 » Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Flow Rate | 0.2 inches |
| Tack-Free Time | 9 minutes |
| Cured: 72 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.07 |
| Durometer, Type A | 30 |
| Tensile Strength | 700 psi (4.8 MPa) |
| Elongation | 560% |
| Stress at 200% Strain | 170 psi (1.2 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED-1511 » Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Tack-Free Time | 12 minutes |
| Cured: 72 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.12 |
| Durometer, Type A | 25 |
| Tensile Strength | 1440 psi (9.9 MPa) |
| Elongation | 680% |
| Tear Strength | 95 ppi (16.7 kN/m) |
| Stress at 200% Strain | 130 psi (0.89 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED-2000 » Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate† | 2.5 g/min. |
| Tack-Free Time | 12 minutes |
| Cured: 72 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.08 |
| Durometer, Type A | 25 |
| Tensile Strength | 1,375 psi (9.5 MPa) |
| Elongation | 800% |
| Tear Strength | 80 ppi (14.1 kN/m) |
| Stress at 200% Strain | 110 psi (0.76 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
† Performed using a Semco model 250-A pneumatic gun with a 14 gauge nozzle orifice and 90 ± 5 psi air pressure.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
2-Part Adhesives
MED1-4213 » Fast-Cure Silicone Adhesive
| Typical Properties | Result | Metric Conv. |
| Uncured: | ||
| Appearance | Translucent | - |
| Viscosity, Part A | 80,000 cP | 80,000 mPas |
| Work Time, MED1-4213 | 15 minutes | - |
| Work Time, MED2-4213 | 15 hours minimum | - |
| Work Time, MED3-4213 | 60 minutes minimum | - |
| Cured: 24 hours at 25°C (MED1-4213 & MED3-4213) | ||
| Cured: 15 minutes at 150°C (MED2-4213) | ||
| Specific Gravity | 1.12 | - |
| Durometer, Type A, MED1-4213, MED3-4213 | 20 | - |
| Durometer, Type A, MED2-4213 | 15 | - |
| Tensile Strength | 1,000 psi | 6.9 Mpa |
| Elongation | 800% | - |
| Tear Strength | 130 | 23.0 kN/m |
MED2-4213 » Fast-Cure Silicone Adhesive
| Typical Properties | Result | Metric Conv. |
| Uncured: | ||
| Appearance | Translucent | - |
| Viscosity, Part A | 80,000 cP | 80,000 mPas |
| Work Time, MED1-4213 | 15 minutes | - |
| Work Time, MED2-4213 | 15 hours minimum | - |
| Work Time, MED3-4213 | 60 minutes minimum | - |
| Cured: 24 hours at 25°C (MED1-4213 & MED3-4213) | ||
| Cured: 15 minutes at 150°C (MED2-4213) | ||
| Specific Gravity | 1.12 | - |
| Durometer, Type A, MED1-4213, MED3-4213 | 20 | - |
| Durometer, Type A, MED2-4213 | 15 | - |
| Tensile Strength | 1,000 psi | 6.9 Mpa |
| Elongation | 800% | - |
| Tear Strength | 130 | 23.0 kN/m |
MED3-4213 » Fast-Cure Silicone Adhesive
| Typical Properties | Result | Metric Conv. |
| Uncured: | ||
| Appearance | Translucent | - |
| Viscosity, Part A | 80,000 cP | 80,000 mPas |
| Work Time, MED1-4213 | 15 minutes | - |
| Work Time, MED2-4213 | 15 hours minimum | - |
| Work Time, MED3-4213 | 60 minutes minimum | - |
| Cured: 24 hours at 25°C (MED1-4213 & MED3-4213) | ||
| Cured: 15 minutes at 150°C (MED2-4213) | ||
| Specific Gravity | 1.12 | - |
| Durometer, Type A, MED1-4213, MED3-4213 | 20 | - |
| Durometer, Type A, MED2-4213 | 15 | - |
| Tensile Strength | 1,000 psi | 6.9 Mpa |
| Elongation | 800% | - |
| Tear Strength | 130 | 23.0 kN/m |
Color Masterbatches
MED-4800 » OVERVIEW Color Masterbatch for Liquid Silicone Elastomers
| Typical Properties | Result |
| Appearance | |
| MED-4800-1 | White |
| MED-4800-2 | Black |
| MED-4800-3 | Red |
| MED-4800-4 | Orange |
| MED-4800-5 | Yellow |
| MED2-4800-6 | Green |
| MED-4800-6 | Dark Green |
| MED1-4800-7 | Blue |
| MED-4800-7 | Dark Blue |
| MED3-4800-8 | Violet |
| MED50-4800-1 | Translucent White |
| MED50-4800-2 | Translucent Black |
| MED50-4800-3 | Translucent Red |
| MED50-4800-4 | Translucent Orange |
| MED50-4800-5 | Translucent Yellow |
| MED52-4800-6 | Translucent Green |
| MED50-4800-6 | Translucent Dark Green |
| MED51-4800-7 | Translucent Blue |
| MED50-4800-7 | Translucent Dark Blue |
| MED53-4800-8 | Translucent Violet |
| Cytotoxicity (Mixed and cured with NuSil Technology MED series LSR) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4800-1 » Color Masterbatch for Liquid Silicone Elastomers ‑ White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4800-2 » Color Masterbatch for Liquid Silicone Elastomers ‑ Black
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Black |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4800-3 » Color Masterbatch for Liquid Silicone Elastomers ‑ Red
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Red |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4800-4 » Color Masterbatch for Liquid Silicone Elastomers ‑ Orange
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Orange |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4800-5 » Color Masterbatch for Liquid Silicone Elastomers ‑ Yellow
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Yellow |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4800-6 » Color Masterbatch for Liquid Silicone Elastomers ‑ Dark Green
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Dark Green |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4800-7 » Color Masterbatch for Liquid Silicone Elastomers ‑ Dark Blue
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Dark Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED1-4800-7 » Color Masterbatch for Liquid Silicone Elastomers ‑ Blue
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED2-4800-6 » Color Masterbatch for Liquid Silicone Elastomers ‑ Light Green
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Light Green |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED3-4800-8 » Color Masterbatch for Liquid Silicone Elastomers ‑ Violet
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Violet |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4800-1 » Color Masterbatch for Liquid Silicone Elastomers ‑ Translucent White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent White |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4800-2 » Color Masterbatch for Liquid Silicone Elastomers ‑ Translucent Black
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Black |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4800-3 » Color Masterbatch for Liquid Silicone Elastomers ‑ Translucent Red
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Red |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4800-4 » Color Masterbatch for Liquid Silicone Elastomers ‑ Translucent Orange
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Orange |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4800-5 » Color Masterbatch for Liquid Silicone Elastomers ‑ Translucent Yellow
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Yellow |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4800-7 » Color Masterbatch for Liquid Silicone Elastomers ‑ Translucent Dark Blue
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Dark Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED51-4800-7 » Color Masterbatch for Liquid Silicone Elastomers ‑ Translucent Blue
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
HCR
MED-4502 » OVERVIEW Color Masterbatch for High Consistency Silicone Elastomers
| Typical Properties | Result |
| Appearance | |
| MED-4502-1 | White |
| MED-4502-2 | Black |
| MED-4502-3 | Red |
| MED-4502-4 | Orange |
| MED-4502-5 | Yellow |
| MED2-4502-6 | Green |
| MED-4502-6 | Dark Green |
| MED1-4502-7 | Blue |
| MED-4502-7 | Dark Blue |
| MED3-4502-8 | Violet |
| Cytotoxicity (Mixed and cured with NuSil Technology MED series HCR) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4502-1 » Color Masterbatch for High Consistency Silicone Elastomers ‑ White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4502-2 » Color Masterbatch for High Consistency Silicone Elastomers ‑ Black
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Black |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4502-3 » Color Masterbatch for High Consistency Silicone Elastomers ‑ Red
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Red |
| Tissue Culture (cytotoxicty Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4502-4 » Color Masterbatch for High Consistency Silicone Elastomers ‑ Orange
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Orange |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4502-5 » Color Masterbatch for High Consistency Silicone Elastomers ‑ Yellow
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Yellow |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4502-6 » Color Masterbatch for High Consistency Silicone Elastomers ‑ Dark Green
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Green |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4502-7 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Blue
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED1-4502-7 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Blue
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED2-4502-6 » Color Masterbatch for High Consistency Silicone Elastomers ‑ Light Green
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Light Green |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED3-4502-8 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Violet
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Violet |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Radio Opaque
MED2-4502 » Barium Sulfate Healthcare Silicone Masterbatch ‑ White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Plasticity | 218 mils (5.5 mm) |
| Non-Volatile Content | 99% |
| Specific Gravity | 2.31 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED2-4800 » Barium Sulfate Healthcare Silicone Masterbatch ‑ White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Non-Volatile Content | 98.1% |
| Specific Gravity | 1.55 |
| Cured: 5 minutes at 150 °C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
For further information, please see Mixing Masterbatches
Guidelines for Mixing a Barium Sulfate Masterbatch Into a Silicone Product.
MED3-4502 » Titanium Dioxide Healthcare Silicone Color Masterbatch ‑ White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Plasticity | 87 mils (2.2 mm) |
| Non-Volatile Content | 99% |
| Specific Gravity | 2.28 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED3-4800 » Titanium Dioxide Healthcare Silicone Color Masterbatch ‑ White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Non-Volatile Content | 98% |
| Specific Gravity | 1.55 |
| Cured: 5 minutes at 150 °C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Dispersions
MED-6670 » Low Coefficient of Friction Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance, Part A | Translucent |
| Appearance, Part B | Translucent to Opaque |
| Zahn Cup Viscosity, Cup #2 | 16 seconds |
| Percent Solids, Mixed | 25% |
| Cured: 5 minutes minimum at ambient temperature and humidity, then 5 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions: 
1-Part Dispersions
MED-6605 » RTV Cure Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content | 29% |
| Viscosity | 700 cP (700 mPas) |
| Cured: 5 days at ambient temperature and humidity | |
| Specific Gravity | 1.09 |
| Durometer, Type A | 25 |
| Tensile Strength | 1,500 psi (10.3 MPa) |
| Elongation | 980% |
| Tear Strength | 120 ppi (21.1 kN/m) |
| Stress at 300% Strain | 110 psi (0.7 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED-6655 » RTV Fluorosilicone Dispersion
NuSil Technology's MED-6655 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Opaque White |
| Non-Volatile Content | 60% |
| Viscosity | 700 cP (700 mPas) |
| Cured: 72 hours at ambient temp. and humidity | |
| Appearance | Translucent |
| Durometer, Type A | 35 |
| Tensile Strength | 775 psi (5.3 MPa) |
| Elongation | 425% |
| Tear Strength | 45 ppi (7.9 kN/m) |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Important document: Additional information for Dispersions:
MED6-6606 » RTV Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content | 30% |
| Viscosity | 95 cP (95 mPas) |
| Cured: 72 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 20 |
| Tensile Strength | 1,190 psi (8.3 MPa) |
| Elongation | 800% |
| Tear Strength | 115 ppi (20.3 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
2-PartDispersions
MED-6400 » Addition Cure Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content | 35% |
| Viscosity | 860 cP (860 mPas) |
| Cured: 30 minutes at 25°C (77°F), 45 minutes at 75°C (167°F), and 135 minutes at 150°C (302°F) | |
| Durometer, Type A | 30 |
| Refractive Index | 1.43 |
| Tensile Strength | 1,600 psi (11.3 MPa) |
| Elongation | 850% |
| Tear Strength | 160 ppi (28.2 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED-6600 » Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content | 35% |
| Viscosity | 350 cP (350 mPas) |
| Cured: 30 minutes at 25°C (77°F), 45 minutes at 75°C (167°F), and 135 minutes at 150°C (302°F) | |
| Refractive Index | 1.465 |
| Durometer, Type A | 25 |
| Tensile Strength | 1,200 psi (8.22 MPa) |
| Elongation | 800% |
| Tear Strength | 160 ppi (28.2 kN/m) |
| Stress at 300% Strain | 300 psi (2.0 kV/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED-6601 » Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Cured: 30 minutes at 25°C (77°F), 45 minutes at 75°C (167°F), and 135 minutes at 150°C (302°F) 100pph:1pph:1pph:234pph* (Part A: Part B: Part C: Xylene) | |
| Durometer, Type A | 24 |
| Tensile Strength | 1,200 psi (8.3 MPa) |
| Elongation | 800% |
| Tear Strength | 150 ppi (26.4 kN/m) |
| Stress at 300% Strain | 320 psi (2.2 kV/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED-6615 » Addition Cure Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content, Part A | 33 % |
| Non-Volatile Content, Part B | 31 % |
| Viscosity | A: 39 cP / B: 93 cP |
| Cured: 30 minutes minimum at ambient temperature and humidity, 45 minutes at 75°C (167°F), and 15 minutes at 150°C (302°F) | |
| Durometer, Type 00 | 72 |
| Tensile Strength | 1,060 psi (7.3 MPa) |
| Elongation | 750 % |
| Tear Strength | 120 ppi (21.1 kN/m) |
| Stress at 100%Strain | Flowable / Self Leveling |
| Stress @ Strain | 65 psi / (0.45 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED-6640 » Addition Cure High Tear Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content | 20% |
| Viscosity | 3,000 cP (3,000 mPas) |
| Cured: 30 minutes at ambient temperature and humidity, 45 minutes at 75°C (167°F), and 135 minutes at 150°C (302°F) | |
| Refractive Index | 1.41 |
| Durometer, Type A | 40 |
| Tensile Strength | 1,700 psi (11.7 MPa) |
| Elongation | 1000% |
| Tear Strength | 300 ppi (52.9 kN/m) |
| Stress at 100% Strain | 150 psi (1.03 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED-6670 » Low Coefficient of Friction Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance, Part A | Translucent |
| Appearance, Part B | Translucent to Opaque |
| Zahn Cup Viscosity, Cup #2 | 16 seconds |
| Percent Solids, Mixed | 25% |
| Cured: 5 minutes minimum at ambient temperature and humidity, then 5 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
Fluids
MED-360 » Silicone Fluid
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Volatile Content | 0.1% |
| Refractive Index | 1.40 |
| Specific Gravity, Hydrometer | 0.97 |
| Intracutaneous Toxicity | Pass |
| Systemic Toxicity | Pass |
| Pyrogenicity | Pass |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-400 » Silicone Fluid
| Typical Properties | Average Result 350 Cp | Average Result 1,000 Cp | Average Result 12,500 Cp |
| Uncured: | |||
| Appearance | Transparent | Transparent | Transparent to Translucent |
| Volatile Content | 0.3% | 0.2% | 0.1% |
| Specific Gravity, Hydrometer | 1.25 | 1.27 | 1.30 |
| Refractive Index | 1.38 | 1.38 | 1.38 |
| Tissue Culture (Cytotoxicity Testing) | Pass | Pass | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
NuSil® MED-400 may be considered for use in human implantation for a period of greater than 29 days.
MED-420 » Silicone Fluid
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Volatile Content | <0.1% |
| Refractive Index | 1.393 |
| Specific Gravity, Hydrometer | 1.03 - 1.06 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.
MED-460 » Silicone Fluid
NuSil Technology's MED-460 may be considered for use in human implantation for a period of greater than 29 days
| Typical Properties | Average Result 350 Cp | Average Result 1,000 Cp | Average Result 12,500 Cp |
| Uncured: | |||
| Appearance | Translucent | Translucent | Translucent |
| Volatile Content | <0.2 % | <0.2% | <0.3% |
| Refractive Index | 1.382 | 1.382 | 1.383 |
| Tissue Culture (Cytotoxicity Testing) | Pass | Pass | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Gels
MED-6381 » Firm RTV Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity | 10,000 cP (10,000 mPas) |
| Cured: 24 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 0.98 |
| Durometer, Type 00 | 75 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED1-6300 » High Purity Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity | 1,000 cP (1,000 mPas) |
| Volatile Content | 0.10% |
| Specific Gravity | 0.98 |
| Cured: 5 hours at 140°C (284°F) | |
| Penetration (Lab Line Penetrometer, 12g shaft, 1" diameter foot, 15 seconds) | 5 mm |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED2-6300 » High Purity Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 1,000 cP (1,000 mPas) |
| Appearance | Translucent |
| Volatile Content | 0.10% |
| Cured: 5 hours at 140°C (284°F) | |
| Penetration (Lab Line Penetrometer, 19.5g shaft, ¼" diameter foot, 15 seconds. Use a 2 oz. glass squat jar.) | 10 mm |
| Specific Gravity | 0.97 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
‡(Lab Line Penetrometer, 19.5g shaft, ¼" diameter foot, 5 seconds)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED3-6300 » High Purity Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 1,000 cP (1,000 mPas) |
| Appearance | Translucent |
| Volatile Content | 0.10% |
| Cured: 5 hours at 140 °C (284°F) | |
| Penetration (Lab Line Penetrometer, 12g shaft,1" diameter foot, 15 seconds) | 15 mm |
| Specific Gravity | 0.98 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
‡(Lab Line Penetrometer, 12 g shaft, 1" diameter foot, 15 seconds)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED3-6311 » High Purity Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 500 cP (500 mPas) |
| Appearance | Translucent |
| Volatile Content | 0.10% |
| Cured: 3.5 hours at 160°C (320°F) | |
| Penetration (Lab Line Penetrometer, 12g shaft, 1" diameter foot, 5 seconds) | 2.8 mm |
| Specific Gravity | 0.97 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
‡(Lab Line Penetrometer, 12g shaft, 1" diameter foot, 15 seconds)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
High Consistency Rubbers
MED-4770 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 120 mils (3.0 mm) |
| Plasticity, Part B | 110 mils (2.8 mm) |
| Work Time | 2.5 hours |
| Cured: 10 minutes at 138°C (280°F) | |
| Specific Gravity | 1.19 |
| Post-Cured: 4 hours at 177°C (351°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 70 |
| Tensile Strength | 1,415 psi (9.8 MPa) |
| Elongation | 760% |
| Tear Strength | 300 ppi (52.9 kN/m) |
| Stress at 200% Strain | 595 psi (4.1 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Peroxide Cure
MED-2174 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity | 110 mils (2.78 mm) |
| Post Cured: 4 hours at 205°C (401°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.15 |
| Post Cured: 4 hours at 205°C (401°F). Stabilize for 3 hours mini | |
| Durometer, Type A | 50 |
| Tensile Strength | 1,300 psi ( 8.9 MPa) |
| Elongation | 750% |
| Tear Strength | 225 ppi (39.7 kN/m) |
| Stress at 200% Strain | 325 psi (2.2 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4520 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity | 65 mils (1.7 mm) |
| Cured: 5 minutes at 116°C (241°F). Catalyzed using 1.0 pph of CAT-102 (Peroxide) | |
| Specific Gravity | 1.1 |
| Post Cured: 2 hours at 177°C (351°F). Stabilize for 3 hours minimum at ambient temperature and humidity | |
| Durometer, Type A | 28 |
| Tensile Strength | 1,320 psi (9.1 MPa) |
| Elongation | 950% |
| Tear Strength | 135 ppi (23.8 kN/m) |
| Stress at 200% Strain | 105 psi (0.7 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4550 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity | 85 mils (2.2 mm) |
| Cured: 5 minutes at 116°C (241°C). Catalyzed with 1 pph of CAT-102 (Peroxide). | |
| Specific Gravity | 1.16 |
| Post Cured: 2 hours at 177°C (351°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 50 |
| Tensile Strength | 1,400 psi (9.7 MPa) |
| Elongation | 750% |
| Tear Strength | 195 ppi (34.4 kN/m) |
| Stress at 200% Strain | 250 psi (1.7 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4565 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Cured: 5 minutes at 116°C (241°F). Catalyzed with 1 pph of CAT-102 (Peroxide). | |
| Specific Gravity | 1.21 |
| Post Cured: 2 hours at 177°C (351°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 65 |
| Tensile Strength | 1,250 psi (8.6 MPa) |
| Elongation | 700% |
| Tear Strength | 200 ppi (35.3 kN/m) |
| Stress at 200% Strain | 375 psi (2.6 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED4-4515 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity | 90 mils (2.3 mm) |
| Cured: 5 minutes at 116°C (241°F) | |
| Specific Gravity | 1.15 |
| Post Cured: 2 hours at 249°C (480°F). Stab | |
| Durometer, Type A | 50 |
| Tensile Strength | 1,650 psi (11.4 MPa) |
| Elongation | 500% |
| Tear Strength | 100 ppi (17.6 kN/m) |
| Stress at 200% Strain | 400 psi (2.8 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED4-4516 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity | 120 mils (3.0 mm) |
| Cured: 5 minutes at 116°C (241°F) | |
| Specific Gravity | 1.21 |
| Post Cured: 2 hours at 249°C (480°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 70 |
| Tensile Strength | 1,300 psi (9.0 MPa) |
| Elongation | 450% |
| Tear Strength | 130 ppi (22.9 kN/m) |
| Stress at 200% Strain | 500 psi (3.4 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Platinum Cure
MED-4714 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 60 mils (1.5 mm) |
| Plasticity, Part B | 60 mils (1.5 mm) |
| Work Time | 26.0 hours |
| Cured: 10 minutes at 116°C (241°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.08 |
| Durometer, Type A | 15 |
| Tensile Strength | 715 psi (4.9 MPa) |
| Elongation | 1,385% |
| Tear Strength | 155 ppi (27.3 kN/m) |
| Stress at 200% Strain | 40 psi (0.28 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4720 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 65 mils (1.6 mm) |
| Plasticity, Part B | 65 mils (1.6 mm) |
| Work Time | 10.0 hours |
| Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.1 |
| Durometer, Type A | 25 |
| Tensile Strength | 1,390 psi (9.6 MPa) |
| Elongation | 1,240% |
| Tear Strength | 190 ppi (33.5 kN/m) |
| Stress at 200% Strain | 75 psi (0.52 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4725 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 85 mils (2.2 mm) |
| Plasticity, Part B | 80 mils (2.0 mm) |
| Work Time | 2.0 hours |
| Cured: 10 minutes at 171°C (340°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 30 |
| Tensile Strength | 1,395 psi (9.6 MPa) |
| Elongation | 890% |
| Tear Strength | 135 ppi (23.8 kN/m) |
| Stress at 200% Strain | 110 psi (0.76 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4735 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 70 mils (1.8 mm) |
| Plasticity, Part B | 65 mils (1.6 mm) |
| Work Time | 2.0 hours |
| Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 35 |
| Tensile Strength | 1,535 psi (10.6 MPa) |
| Elongation | 1,055% |
| Tear Strength | 195 ppi (34.4 kN/m) |
| Stress at 200% Strain | 180 psi (1.2 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4750 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 95 mils (2.4 mm) |
| Plasticity, Part B | 90 mils (2.3 mm) |
| Work Time | 2.5 hours |
| Cured: 10 minutes at 116°C (239°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.16 |
| Durometer, Type A | 50 |
| Tensile Strength | 1,545 psi (10.7 MPa) |
| Elongation | 1,050% |
| Tear Strength | 270 ppi (47.6 kN/m) |
| Stress at 200% Strain | 300 psi (2.1 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4755 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 85 mils (2.2 mm) |
| Plasticity, Part B | 75 mils (1.9 mm) |
| Work Time | 2.5 hours |
| Cured: 10 minutes at 138°C (280°F) | |
| Specific Gravity | 1.14 |
| Post Cured: 4 hours at 177°C (351°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 55 |
| Tensile Strength | 1,640 psi (11.3 MPa) |
| Elongation | 875% |
| Tear Strength | 310 ppi (54.6 kN/m) |
| Stress at 200% Strain | 490 psi (3.4 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4765 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 125 mils (3.2 mm) |
| Plasticity, Part B | 110 mils (2.8 mm) |
| Work Time | 6.0 hours |
| Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.2 |
| Durometer, Type A | 65 |
| Tensile Strength | 1,240 psi (8.6 MPa) |
| Elongation | 1,005% |
| Tear Strength | 265 ppi (46.7 kN/m) |
| Stress at 200% Strain | 355 psi (2.4 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4780 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 125 mils (3.2 mm) |
| Plasticity, Part B | 100 mils (2.5 mm) |
| Work Time | 8.5 hours |
| Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.2 |
| Durometer, Type A | 80 |
| Tensile Strength | 1,155 psi (8.0 MPa) |
| Elongation | 740% |
| Tear Strength | 225 ppi (39.7 kN/m) |
| Stress at 200% Strain | 450 psi (3.1 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Inks
MED-6608 » OVERVIEW Silicone Coating / Marking Ink Series
| Typical Properties | Average Result | Metric Conv. |
| Uncured: | ||
| Viscosity | 1,150 cP | 1,150 mPas |
| Non-Volatile Content | 70% | - |
| Tack-Free Time | 45 minutes | - |
| Cured: 24 hours minimum at ambient temp. and humidity | ||
| Adhesion* | Pass | - |
| Cured: 7 days minimum at ambient temp. and humidity | ||
| Specific Gravity (white / black) | 1.13 / 1.46 | - |
| Cytotoxicity | Pass | - |
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED-6608-1 » White Silicone Coating / Marking Ink Series
| Typical Properties | Average Result | Metric Conv. |
| Uncured: | ||
| Viscosity | 1,150 cP | 1,150 mPas |
| Non-Volatile Content | 70% | - |
| Tack-Free Time | 45 minutes | - |
| Cured: 24 hours minimum at ambient temp. and humidity | ||
| Adhesion(Primed with MED-160) | Pass | - |
| Cured: 7 days minimum at ambient temp. and humidity | ||
| Specific Gravity (white / black) | 1.13 / 1.46 | - |
| Cytotoxicity | Pass | - |
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED-6608-2 » Black Silicone Coating / Marking Ink Series
| Typical Properties | Average Result | Metric Conv. |
| Appearance | Black | |
| Viscosity | 1,150 cP | 1,150 mPas |
| Non-Volatile Content | 70% | - |
| Tack-Free Time | 80 minutes | - |
| Cured: 24 hours minimum at ambient temp. and humidity | ||
| Adhesion(Primed with MED-160) | Pass | - |
| Cured: 7 days minimum at ambient temp. and humidity | ||
| Specific Gravity | 1.46 | - |
| Cytotoxicity | Pass | - |
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED8-6608-2 » Black Silicone Coating / Marking Ink
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Black |
| Non-Volatile Content | 70% |
| Viscosity | 800 cP (800 mPas) |
| Tack-Free Time | 40 minutes |
| Cured: 7 days minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.83 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
2-Part Inks
MED-6613-1 » Silicone Ink (WHITE)
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Non-Volatile Content, Part A | 65% |
| Non-Volatile Content, Part B | 65% |
| Cured: 5 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6613-2 » Silicone Ink (BLACK)
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Black |
| Non-Volatile Content, Part A | 60% |
| Non-Volatile Content, Part B | 60% |
| Viscosity, Part A | 900 cP (800 mPas) |
| Viscosity, Part B | 800 cP (11,500 mPas) |
| Cured: 5 minutes at 150°C (302°F) | |
| Adhesion | Pass |
| Cured: 30 minutes minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6613-7 » Silicone Ink (DARK BLUE)
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Dark Blue |
| Non-Volatile Content, Part A | 65% |
| Non-Volatile Content, Part B | 65% |
| Cured: 5 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Liquid Silicone Rubbers
MED-4810 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 85 g/min |
| Extrusion Rate†, Part B | 110 g/min |
| Work Time | 70 hours |
| Cured: 5 minutes at 150°C (302°F). St | |
| Specific Gravity | 1.1 |
| Durometer, Type A | 11 |
| Tensile Strength | 700 psi (4.8 MPa) |
| Elongation | 1075% |
| Tear Strength | 65 ppi (11.38 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4820 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 60 g/min |
| Extrusion Rate†, Part B | 90 g/min |
| Work Time | 72 hours |
| Cured: 5 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.14 |
| Durometer, Type A | 20 |
| Tensile Strength | 910 psi (6.3 MPa) |
| Elongation | 875% |
| Tear Strength | 125 ppi (21.89 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4830 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate, Part A† | 160 gpm |
| Extrusion Rate, Part B† | 190 gpm |
| Work Time | >24 hours |
| Cured: 5 minutes at 150°C (302°F). Stabilize for a minimum of 3 hours at ambient temperature and humidity. | |
| Specific Gravity | 1.13 |
| Durometer, Type A | 30 |
| Tensile Strength | 1350 psi (9.3 MPa) |
| Elongation | 750% |
| Tear Strength | 150 ppi (26.27 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4840 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate, Part A† | 160 gpm |
| Extrusion Rate, Part B† | 290 gpm |
| Work Time | >72 hours |
| Cured: 5 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.12 |
| Durometer, Type A | 43 |
| Tensile Strength | 1190 psi (8.2 MPa) |
| Elongation | 560% |
| Tear Strength | 245 ppi (42.91 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® 440 nozzle with a ⅛ orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4842 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Extrusion Rate, Part A† | 145 gpm |
| Extrusion Rate, Part B† | 285 gpm |
| Work Time | >72 hours |
| Cured: 10 minutes at 150° (302°F). | |
| Specific Gravity | 1.17 |
| Durometer, Type A | 44 |
| Tensile Strength | 1070 psi (7.4 MPa) |
| Elongation | 400Game: Quarantine |
| Tear Strength | 250 ppi (44.1 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® 440 nozzle with a ⅛ orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4850 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate, Part A† | 95 g/min |
| Extrusion Rate, Part B† | 105 g/min |
| Work Time | 72 hours |
| Cured: 5 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.14 |
| Durometer, Type A | 50 |
| Tensile Strength | 1455 psi (10.0 MPa) |
| Elongation | 700% |
| Tear Strength | 240 ppi (42.03 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4860 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 65 g/min |
| Extrusion Rate†, Part B | 100 g/min |
| Work Time | 72 hours |
| Cured: 5 minutes at 165°C (329°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.15 |
| Durometer, Type A | 60 |
| Tensile Strength | 1350 psi (9.3 MPa) |
| Elongation | 530% |
| Tear Strength | 255 ppi (44.66 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4870 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 50 g/min |
| Extrusion Rate†, Part B | 65 g/min |
| Work Time | 72 hours |
| Cured: 5 minutes at 165°C (329°F) | |
| Specific Gravity | 1.16 |
| Durometer, Type A | 70 |
| Tensile Strength | 1500 psi (10.3 MPa) |
| Elongation | 415% |
| Tear Strength | 230 ppi (40.28 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4880 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 40 g/min |
| Extrusion Rate†, Part B | 175 g/min |
| Work Time | 70 hours |
| Cured: 5 minutes at 165°C (329°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.16 |
| Durometer, Type A | 80 |
| Tensile Strength | 1030 psi (7.1 MPa) |
| Elongation | 265% |
| Tear Strength | 90 ppi (15.76 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-5440 » Liquid Injection Molding Fluorosilicone Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 40 g/min |
| Extrusion Rate†, Part B | 40 g/min |
| Work Time | >24 hours |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.38 |
| Durometer, Type A | 40 |
| Tensile Strength | 1,250 psi (8.6 MPa) |
| Elongation | 380% |
| Tear Strength | 60 ppi (10.6 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-5820 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 220 g/min |
| Extrusion Rate†, Part B | 220 g/min |
| Work Time | > 24 hours |
| Cured: 5 minutes at 165°C (329°F). | |
| Specific Gravity | 1.08 |
| Durometer, Type A | 19 |
| Tensile Strength | 1,080 psi (7.5 MPa) |
| Elongation | 890% |
| Tear Strength | 90 ppi (15.76 kN/m) |
| Stress at 200% Strain | 90 psi (0.62 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-5830 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 145 g/min |
| Extrusion Rate†, Part B | 145 g/min |
| Work Time | > 24 hours |
| Cured: 5 minutes at 165°C (329°F). | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 30 |
| Tensile Strength | 150 ppi (26.27 kN/m) |
| Elongation | 830% |
| Tear Strength | 1,340 psi (9.2 MPa) |
| Stress at 200% Strain | 160 psi (1.10 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-5840 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 110 g/min |
| Extrusion Rate†, Part B | 115 g/min |
| Work Time | > 24 hours |
| Cured: 5 minutes at 165°C (329°F). | |
| Specific Gravity | 1.12 |
| Durometer, Type A | 40 |
| Tensile Strength | 1,350 psi (9.3 MPa) |
| Elongation | 680% |
| Tear Strength | 160 ppi (28.02 kN/m) |
| Stress at 200% Strain | 300 psi (2.07 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-5850 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 80 g/min |
| Extrusion Rate†, Part B | 65 g/min |
| Work Time | > 72 hours |
| Cured: 5 minutes at 165°C (329°F). | |
| Specific Gravity | 1.14 |
| Durometer, Type A | 50 |
| Tensile Strength | 1,450 psi (10 MPa) |
| Elongation | 550% |
| Tear Strength | 190 ppi (33.27 kN/m) |
| Stress at 200% Strain | 400 psi (2.76 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-5860 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 80 g/min |
| Extrusion Rate†, Part B | 65 g/min |
| Work Time | > 72 hours |
| Cured: 5 minutes at 165°C (329°F). | |
| Specific Gravity | 1.14 |
| Durometer, Type A | 60 |
| Tensile Strength | 1,300 psi (9.0 MPa) |
| Elongation | 425% |
| Tear Strength | 200 ppi (35.03 kN/m) |
| Stress at 200% Strain | 700 psi (4.83 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-5870 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 100 g/min |
| Extrusion Rate†, Part B | 100 g/min |
| Work Time | > 72 hours |
| Cured: 5 minutes at 165°C (329°F). | |
| Specific Gravity | 1.14 |
| Durometer, Type A | 68 |
| Tensile Strength | 1,250 psi (9.2 MPa) |
| Elongation | 400% |
| Tear Strength | 225 ppi (39.40 kN/m) |
| Stress at 200% Strain | 900 psi (6.21 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED50-5338 » Fluorosilicone Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 90 g/min |
| Extrusion Rate†, Part B | 135 g/min |
| Work Time | 16 hours |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.25 |
| Durometer, Type A | 30 |
| Tensile Strength | 650 psi (4.5 MPa) |
| Elongation | 350% |
| Tear Strength | 37 ppi (6.5 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Low Consistency Elastomers
MED-4211 » Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 105,000 cP (105,000 mPas) |
| Viscosity, Part B | 1,500 cP (1,500 mPas) |
| Cured: 3 minutes at 150°C (302°F) Post-Cured: 1 hour at 150°C (302°F). Stabilize for 3 hours at ambient temperature and humidity | |
| Specific Gravity | 1.1 |
| Durometer, Type A | 25 |
| Tensile Strength | 685 psi (4.7 MPa) |
| Elongation | 530% |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4244 » Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 130,000 cP (130,000 mPas) |
| Viscosity, Part B | 360 cP (360 mPas) |
| Work Time | 4 hours |
| Cured: 3 minutes at 177°C (376°F) | |
| Post-Cured: 1 hour at 150°C (328°C) | |
| Specific Gravity | 1.1 |
| Durometer, Type A | 40 |
| Tensile Strength | 865 psi (6.0 MPa) |
| Elongation | 350% |
| Tear Strength | 150 ppi (26.4 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4286 » Ultra-Soft Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity, Part A | 8,200 cP (8,200 mPas) |
| Viscosity, Part B | 4,500 cP (4,500 mPas) |
| Work Time | 17.5 hours |
| Cured: 45 minutes at 150°C (302°F) | |
| Durometer, (Type 000) | 55 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6210 » Optically Clear Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 19,000 cP (19,000 mPas) |
| Viscosity, Part B | 13,000 cP (13,000 mPas) |
| Work Time | 4 hours |
| Refractive Index | 1.43 |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.05 |
| Durometer, Type A | 50 |
| Tensile Strength | 930 psi (6.4 MPa) |
| Elongation | 140% |
| Tear Strength | 35 ppi (6.1 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6215 » Optically Clear Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Viscosity, Part A | 5,500 cP (5,500 mPas) |
| Viscosity, Part B | 95 cP (95 mPas) |
| Work Time | 5 hours |
| Cured: 15 minutes at 150°C (302°F) | |
| Specific Gravity | 1.03 |
| Durometer, Type A | 50 |
| Tensile Strength | 1,250 psi (8.6 MPa) |
| Elongation | 100% |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6219 » Clear High Durometer Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Viscosity, Part A | 28,000 cP (28,000 mPas) |
| Viscosity, Part B | 23,000 cP (23,000 mPas) |
| Work Time | 2.5 hours |
| Cured: 2 hours at 50°C (122°F) | |
| Specific Gravity | 1.07 |
| Durometer, Type A | 75 |
| Tensile Strength | 1,300 psi (9.0 MPa) |
| Elongation | 65% |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6233 » Optically Clear Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Viscosity, Part A | 88,000 cP (88,000 mPas) |
| Viscosity, Part B | 59,000 cP (59,000 mPas) |
| Refractive Index, Part A | 1.41 |
| Refractive Index, Part B | 1.41 |
| Work Time | 52 hours |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.04 |
| Durometer, Type A | 50 |
| Tensile Strength | 740 psi (5.1 MPa) |
| Elongation | 380% |
| Tear Strength | 80 ppi (14.1 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6820 » Optically Clear Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Viscosity, Part A | 78,000 cP (78,000 mPas) |
| Viscosity, Part B | 54,000 cP (54,000 mPas) |
| Work Time | 4.5 hours |
| Cured: 30 minutes at 150°C (302°F) | |
| Durometer, Type A | 40 |
| Tensile Strength | 670 psi (4.6 MPa) |
| Elongation | 210% |
| Tear Strength | 40 ppi (7.6 kN/m) |
| Refractive Index | 1.436 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED2-4420 » Fast Cure Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 22,000 cP (22,000 mPas) |
| Viscosity, Part B | 17,000 cP (17,000 mPas) |
| Work Time | 3 minutes |
| Cured: 15 minutes at 150°C (302°F) | |
| Specific Gravity | 1.07 |
| Durometer, Type A | 20 |
| Tensile Strength | 585 psi (4.4 MPa) |
| Elongation | 500% |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED3-4420 » Fast Cure Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 91,250cP (91,250mPas) |
| Viscosity, Part B | 74,150cP (74,165mPas) |
| Work Time | 15 minutes |
| Cured: 30 +/- 5 minutes at 150 +/- 5°C | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 23 |
| Tensile Strength | 1,000psi (6.9MPa) |
| Elongation | 600% |
| Tear Strength | 75ppi (13.2kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED4-4420 » Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 27,000 cP (27,000 mPas) |
| Viscosity, Part B | 19,500 cP (19,500 mPas) |
| Work Time | 35 minutes |
| Cured: 15 minutes at 150°C (302°F) | |
| Durometer, Type A | 17 |
| Tensile Strength | 700 psi (4.8 MPa) |
| Elongation | 600% |
| Tear Strength | 35 ppi (6.2 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Primers
MED-160 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Percent Solids | 4.0% |
| Specific Gravity, Pycnometer | 0.77 |
| Devolatilized: 2 hours at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Additional information for Primers: Application and Storage Recommendations PDF
MED-162 » Silicone Primer For Polycarbonates
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Percent Solids | 15% |
| Specific Gravity, Pycnometer | 0.79 |
| Cured: 2 hours minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Additional information for Primers: Application and Storage Recommendations PDF
MED-163 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Specific Gravity, Pycnometer | 0.78 |
| Percent Solids | 15% |
| Devolatilized: 2 hours minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Additional information for Primers: Application and Storage Recommendations PDF
MED-164 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Specific Gravity, Pycnometer | 0.79 |
| Percent Solids | 10% |
| Devolatilized: 2 hours minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Additional information for Primers: Application and Storage Recommendations PDF
MED-166 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Specific Gravity, Pycnometer | 0.8 |
| Percent Solids | 6.5% |
| Devolatilized: 1 hour minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Additional information for Primers: Application and Storage Recommendations PDF
MED1-161 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Specific Gravity, Pycnometer | 0.77 |
| Percent Solids | 4.5% |
| Devolatilized: 2 hours minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.
Additional information for Primers: Application and Storage Recommendations PDF
Biomaterials
Advanced Technologies
Tubing
Equipment